Green synthesis, characterization and antimicrobial activities of zinc oxide nanoparticles from the leaf extract of Azadirachta indica (L.)

The antibacterial properties of zinc oxide nanoparticles were investigated using both gram-positive and gram-negative microorganisms. These studies demonstrate that ZnO nanoparticles have a wide range of antibacterial activities toward various microorganisms that are commonly found in environmental settings. The antibacterial activity of the ZnO nanoparticles was inversely proportional to the size of the nanoparticles in S. aureus. Surprisingly, the antibacterial activity did not require specific UV activation using artificial lamps, rather activation was achieved under ambient lighting conditions. Northern analyses of various reactive oxygen species (ROS) specific genes and confocal microscopy suggest that the antibacterial activity of ZnO nanoparticles might involve both the production of reactive oxygen species and the accumulation of nanoparticles in the cytoplasm or on the outer membranes. Overall, the experimental results suggest that ZnO nanoparticles could be developed as antibacterial agents against a wide range of microorganisms to control and prevent the spreading and persistence of bacterial infections.

In the present investigation, we have described the green biosynthesis of ZnO nanoparticles (NPs) by using Solanum nigrum as capping agent. The functionalization of ZnO particles through S. nigrum leaf extract mediated bioreduction of ZnO was investigated through UV-Vis DRS, photoluminescence (PL), X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) spectroscopy, Field Emission Scanning Electron Microscopy (FE-SEM), Transmission Electron Microscopy (TEM), thermal gravimetric-differential thermal analysis (TG-DTA), X-ray photoelectron spectroscopy (XPS) and antibacterial activities. UV-Vis-DRS studies revealed that the indirect band gap 3.38 eV and photoluminescence study reveals the blue emission at 402, 447, 469 and 483 nm and the green emission at 529 nm respectively. In addition, the synthesized NPs are wurtzite hexagonal structure with an average grain size lies between 20 and 30 nm were found from XRD analysis. Further, FT-IR spectra revealed the functional groups and the presence of protein as the stabilizing agent for surrounding the ZnO NPs. The diameter of the NPs in the range of 20-30 nm was found from FE-SEM study. TEM analysis was investigated the ZnO NPs as a quasi-spherical in shape and their diameter at around 29.79 nm. Finally, the current study has clearly demonstrated that the particle size variations and surface area to volume ratios of ZnO NPs are responsible for significant higher antibacterial activities. Further, the present investigation suggests that ZnO NPs has the potential applications for various medical and industrial fields so, that the investigation is so useful and helpful to the scientific communities.