Fracture Resistance of Three Post Types in the Restoration of Anterior Primary Teeth

There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

Abstract

Background:

Extensive restorative treatments of anterior primary teeth are challenging in pediatric dentistry.

Objective:

This study aimed to compare the fracture resistance of three post types for restoring the anterior primary teeth.

Methods:

This in-vitro study was carried out on 90 extracted maxillary anterior primary teeth with intact roots. They were randomly allocated into six groups to be restored with conventional composite resin post, X-tra fill composite resin post, Tetric N Ceram composite resin post, prefabricated glass fiber post with conventional composite build-up, prefabricated glass fiber post with X-tra fill composite build-up, and prefabricated glass fiber post with Tetric N Ceram composite build up. The samples were polished and placed in acrylic resin blocks with 1 mm of part of cervical root being out, thermocycled (×5000) and tested for fracture resistance. Intra-class correlation test, Kruskal-Wallis test and one-way ANOVA were used for statistical analyses (α=0.05).

Results:

The mean fracture resistance was significantly different among the six groups. It was the highest in prefabricated glass fiber post with conventional composite build-up (418.64 N), prefabricated glass fiber post with X-tra fill composite build-up (403.63 N) and prefabricated glass fiber post with Tetric N Ceram composite build up (361.63 N); and the lowest in Tetric N Ceram group (280.65 N). The groups were significantly different concerning the fracture strength and fracture state.

Conclusion:

Since the anterior teeth restored with prefabricated glass fiber posts were far more fracture resistant, and prefabricated glass fiber posts can be promisingly used for the restoration of anterior primary teeth.

Related collections

Most cited references 27

Record: found
Abstract: found
Article: not found

Fracture strength after dynamic loading of endodontically treated teeth restored with different post-and-core systems.

Frank Butz, J R Strub, Amr Hussein … (2002)

Prefabricated metal and ceramic posts can be used with direct or indirect cores as an alternative to the conventional cast post and core. It is unclear how the fracture strength of zirconia posts with composite or ceramic cores and titanium posts with composite cores compares to the fracture strength of gold posts and cores after dynamic loading. This study compared the fracture strength of endodontically treated, crowned maxillary incisors with limited ferrule length and different post-and-core systems after fatigue loading. Sixty-four caries-free, human maxillary central incisors were divided into 4 groups. After root canal treatment, Group 1 was restored with titanium posts and composite cores, Group 2 with zirconia posts and composite cores, and Group 3 with zirconia posts and heat-pressed ceramic cores. Teeth restored with cast-on gold posts and cores served as the controls (Group 4). Teeth were prepared with a circumferential shoulder including a 1 to 2 mm ferrule; all posts were cemented with an adhesive resin cement, restored with complete-coverage crowns, and exposed to 1.2 million load cycles (30 N) in a computer-controlled chewing simulator. Simultaneous thermocycling between 5 degrees C and 55 degrees C was applied for 60 seconds with an intermediate pause of 12 seconds. All specimens that did not fracture during dynamic loading were loaded until fracture in a universal testing machine at a crosshead speed of 1.5 mm/min; loads were applied at an angle of 130 degrees at the incisal edge. Fracture loads (N) and modes (repairable or catastrophic) were recorded. The Kruskal-Wallis test was used to compare fracture loads among the 4 test groups. Analyses were conducted both with and without the specimens that failed during the chewing simulation. A Fisher exact test was performed to detect group differences in fracture modes. A significance level of P<.05 was used for all comparisons. The following survival rates were recorded after the chewing simulation: 93.8% (Group 1), 93.8% (Group 2), 100% (Group 3), and 87.5% (Group 4). The median fracture strengths for Groups 1 to 4 were 450 N, 503 N, 521 N, and 408 N, respectively. No significant differences were detected among the groups. The use of zirconia posts resulted in a nonsignificant lower number of catastrophic root fractures. Within the limitations of this study, the results suggest that zirconia posts with ceramic cores can be recommended as an alternative to cast posts and cores. If a chairside procedure is preferred, zirconia or titanium posts with composite cores can be used. Clinical trials are required to verify these in vitro results.

0 comments Cited 32 times – based on 0 reviews      Review now

Bookmark

Record: found
Abstract: found
Article: found

Is Open Access

Dental fiber-post resin base material: a review

Aashwini Lamichhane, CHUN XU, Fu-Qiang Zhang (2014)

Teeth that have short clinical crown, which are not alone enough to support the definitive restoration can be best treated using the post and core system. The advantages of fiber post over conventional metallic post materials have led to its wide acceptance. In addition to that the combination of aesthetic and mechanical benefits of fiber post has provided it with a rise in the field of dentistry. Also the results obtained from some clinical trials have encouraged the clinicians to use the fiber posts confidently. Fiber posts are manufactured from pre-stretched fibers impregnated within a resin matrix. The fibers could that be of carbon, glass/silica, and quartz, whereas Epoxy and bis-GMA are the most widely used resin bases. But recently studies are also found to be going on for polyimide as possible material for the fiber post resin base as a substitute for the conventional materials.

0 comments Cited 31 times – based on 0 reviews      Review now

Bookmark

Record: found
Abstract: found
Article: found

Is Open Access

A comparative evaluation of fracture resistance of endodontically treated teeth restored with different post core systems - an in-vitro study

Chetana Makade, Ganesh K. Meshram, Manjusha Warhadpande … (2011)

PURPOSE To compare the fracture resistance and the mode of failure of endodontically treated teeth restored with different post-core systems. MATERIALS AND METHODS Root canal treatment was performed on 40 maxillary incisors and the samples were divided into four groups of 10 each. For three experimental groups post space preparation was done and teeth were restored with cast post-core (Group B), stainless steel post with composite core (Group C) and glass fiber post with composite core using adhesive resin cement (Group D). Control group (A) samples were selected with intact coronal structure. All the samples were prepared for ideal abutment preparation. All the samples were subjected to a load of 0.5 mm/min at 130° until fracture occurred using the universal testing machine. The fracture resistance was measured and the data were analyzed statistically. The fracture above the embedded resin was considered to be favorable and the fracture below the level was considered as unfavorable. The statistical analysis of fracture resistance between different groups was carried out with t-test. For the mode of failure the statistical analysis was carried out by Kruskal-Wallis test and Chi-Square test. RESULTS For experimental group Vs control group the fracture resistance values showed significant differences (P<.05). For the mode of failure the chi-square value is 16.1610, which means highly significant (P=.0009) statistically. CONCLUSION Endodontically treated teeth without post core system showed the least fracture resistance demonstrating the need to reinforce the tooth. Stainless steel post with composite core showed the highest fracture resistance among all the experimental groups. Teeth restored with the Glass fiber post showed the most favorable fractures making them more amenable to the re-treatment.